Zero Temperature Coefficient .TAU.f and Sinterability of Forsterite Ceramics by Rutile Addition
https://nitech.repo.nii.ac.jp/records/5185
https://nitech.repo.nii.ac.jp/records/518587df9b1d-212d-41e3-b964-486f7a4a26fb
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
本文_fulltext (369.8 kB)
|
(c) 2004 The Ceramic Society of Japan
|
| Item type | 学術雑誌論文 / Journal Article(1) | |||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2012-11-06 | |||||||||||||||
| タイトル | ||||||||||||||||
| タイトル | Zero Temperature Coefficient .TAU.f and Sinterability of Forsterite Ceramics by Rutile Addition | |||||||||||||||
| 言語 | en | |||||||||||||||
| 言語 | ||||||||||||||||
| 言語 | eng | |||||||||||||||
| 資源タイプ | ||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||
| 資源タイプ | journal article | |||||||||||||||
| 著者 |
Tsunooka, Tsutomu
× Tsunooka, Tsutomu
× Sugiyama, H
× Kakimoto, Ken-ichi
× Osato, Hitoshi
× Ogawa, H
|
|||||||||||||||
| 著者別名 | ||||||||||||||||
| 姓名 | 角岡, 勉 | |||||||||||||||
| 著者別名 | ||||||||||||||||
| 姓名 | 柿本, 健一 | |||||||||||||||
| 著者別名 | ||||||||||||||||
| 姓名 | 大里, 齊 | |||||||||||||||
| bibliographic_information |
en : Journal of the Ceramic Society of Japan 巻 112, 号 1305, p. S1637-S1640, 発行日 2004-05-01 |
|||||||||||||||
| 出版者 | ||||||||||||||||
| 出版者 | The Ceramic Society of Japan | |||||||||||||||
| 言語 | en | |||||||||||||||
| ISSN | ||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||
| 収録物識別子 | 0914-5400 | |||||||||||||||
| item_10001_source_id_32 | ||||||||||||||||
| 収録物識別子タイプ | NCID | |||||||||||||||
| 収録物識別子 | AN10040326 | |||||||||||||||
| 出版タイプ | ||||||||||||||||
| 出版タイプ | VoR | |||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||||||||
| 内容記述 | ||||||||||||||||
| 内容記述タイプ | Other | |||||||||||||||
| 内容記述 | The temperature coefficient (.TAU.f) of the resonant frequency for pure forsterite (Mg2SiO4) ceramics was negative in the range from -60 to -70ppm/.DEG.C.. To adjust the .TAU.f value to zero, rutile (TiO2) with the high .TAU.f (450ppm/.DEG.C.) was added. When sintering temperature was selected as low as possible, TiO2 remained in the forsterite specimen, which raised .TAU.f from a negative to positive values. For instance, the 30wt% TiO2 added forsterite ceramics sintered at 1200.DEG.C. yield a high density (3.3g/cm3), which same as that of the same forsterite ceramics sintered at 1350.DEG.C.. A part of added TiO2 works for sintering aid and residual ones do for lowering the .TAU.f value. Forsterite ceramics have .TAU.f=0ppm/.DEG.C., .EPSILON.r=11 and Q f=82000GHz, when they contains 24wt% of TiO2 and sintered at 1200/.DEG.C. for 2h. | |||||||||||||||