@article{oai:nitech.repo.nii.ac.jp:00004034,
 author = {大門, 啓志},
 issue = {1136},
 journal = {Journal of the Ceramic Society of Japan},
 month = {Apr},
 note = {Rod-like particles of Al_2TiO_5-MgTi_2O_5 solid solutions were synthesized by heating mixed powders of MgO, Al_2O_3 and TiO_2 above 1050℃ in the presence of 10 atom% mixed fluoride of MgF_2 and AlF_3. The rod diameter decreased with decreasing synthesis temperatures while the aspect ratio increased. At a certain temperature the rod diameter increased with increasing MgTi_2O_5 contents while the aspect ratio decreased. A sinterable powder composed of rod-like particles, in which rod diameter and aspect ratio were about 2 μm and about 4, respectively, was obtained by heating the raw materials containing 50% MgTi_2 O_5 at 1200℃. Using the rod-like particles, a sintered body of a highly oriented solid solution with the Lotgering's index f_<&parsl;a> of 0.76, was obtained. Thermal expansion anisotropy was observed, and the hysteresis of the expansion-shrinkage behavior was smaller than that of the sintered body without preferred orientation., application/pdf},
 pages = {365--369},
 title = {Al_2TiO_5一MgTi_20_5系配向焼結体の調製と熱膨張特性},
 volume = {98},
 year = {1990},
 yomi = {ダイモン, ケイジ}
}