@article{oai:nitech.repo.nii.ac.jp:00005248,
 author = {Yokota, Takeshi and Yan, M. L. and Xu, Ying F. and Gao, L. and Zhang, R. and Nicholl, L. and Yuan, L. and Skomski, R. and Sellmyer, D. J. and Liou, S. H. and Lai, Chih Huang and Yang, Cheng Han and Huang, Sheng Huang},
 issue = {10},
 journal = {JOURNAL OF APPLIED PHYSICS},
 month = {May},
 note = {We investigated magnetic properties and L10 phase formation of FePt films by rapid thermal annealing (RTA) and high current-density ion-beam irradiation. The sample prepared by RTA at 550°C has (001) texture and strong magnetic perpendicular anisotropy with Hc equal to 6 kOe. The sample irradiated at 5.04 μA/cm2 has Hc equal to 10 kOe but has isotropic magnetic properties due to the (111) texture. The magnetic correlation length of the ion-irradiated sample was about twice as large as that of the RTA sample. This may be due to the inhomogeneity of the L10 phase formation in the ion-irradiated film., application/pdf},
 pages = {10H306-1--10H306-3},
 title = {Magnetic properties and L10 phase formation of FePt films prepared by high current-density ion-beam irradiation and rapid thermal annealing methods},
 volume = {97},
 year = {2005}
}