 author = {Hashimoto, Shinobu and Sato, Fumiharu and Honda, Sawao and Awaji, Hideo and Fukuda, Koichiro},
 issue = {1319},
 journal = {Journal of the Ceramic Society of Japan},
 month = {Jul},
 note = {Fine leucite powder with an average diameter of 0.2μm was fabricated by the low-temperature synthesis method for leucite using natural mineral potash feldspar as the major raw material, followed by ball milling. A sintered leucite body with a 99.0% relative density was obtained by heating the leucite powder cylindrical pellet at 1250℃ for 1h. The mechanical properties of this dense leucite body were determined. The bending strength, fracture toughness, elastic modulus and Vickers hardness of the body were 173MPa, 2.3MPa・m^<1/2>, 63GPa and 5.3GPa, respectively., application/pdf},
 pages = {488--490},
 title = {Fabrication and Mechanical Properties of Sintered Leucite Body},
 volume = {113},