@article{oai:nitech.repo.nii.ac.jp:00005334,
 author = {橋本, 忍 and 武田, はやみ and 奥田, 篤史 and 上林, 晃 and 本多, 沢雄 and 淡路, 英夫 and 福田, 功一郎},
 issue = {1340},
 journal = {Journal of the Ceramic Society of Japan},
 month = {Apr},
 note = {According to phase-contrast microscope analysis based on the JIS A 1481: 2006, chrysotile in the asbestos-containing building material waste was not detected after heating at 800℃ for over 2 h. The asbestos-cement which was ground to below 180μm after heating asbestos-containing building material waste at 800℃ for 3 h was added into OPC to fabricate secondary cement product. When 50 mass% of the asbestos-cement was added to OPC, the compressive strength of the secondary cement product after 7 days was 32 MPa. Further chrysotile was not detected in the secondary cement product using phase contrast microscope analysis., application/pdf},
 pages = {290--293},
 title = {アスベストを含む廃建材の無害化とセメント製品への適用},
 volume = {115},
 year = {2007},
 yomi = {ハシモト, シノブ and ホンダ, サワオ and フクダ, コウイチロウ}
}